PRODUCT NAME Chlorosulphonated Polythylene Coat Slj53

BRIEF   One Pack Chlorosulphonated Polythylene Coating

FEATURES 
-Good adhesion, hardness and gloss
-Good burning and mildew resistance
 -Good water, corrosion and permeation resistance 
-Can be exposed to atmosphere and immersed in water
-Resistance to low temperature to -40℃

RESISTANCE GUIDE
HEAT RESISTANCE  Up to 120℃ dry heat 
WEATHERABILITY   Good weatherability and ozone proof
SOLVENTS           Resists splash and spillage of aliphatic solvents and mineral oil
 ACIDS              Suitable for splash and spillage exposure to most solutions of inorganic acids.
 ALKALIS            Suitable for splash and spillage of most alkalis
 SALTS              Suitable for splash and spillage of most alkali salts
 WATER              Excellent resistance to splash and spillage of fresh and salt water
 ABRASION           Good when fully cured.
 
USES:Suitable for the protection of steel structure and concrete surface under  industrial, marine or other chemical medium environments.
 
TYPICAL PROPERTIES AND APPLICATION DATA
 COLOR                         Topcoat, Color       Primer, Iron Red
 DENSITY                       1.35g/cm3
 SOLIDS BY VOLUME            38%
 SPREADING RATE               6.0 m2/kg (40um DFT)
 DRYING TIME(23℃)             Touch  ≤2 Hr    Handle ≤24 Hr    Full cure 7Days
 OVERCOAT INTERVAL(23℃)      Min 8 Hr  
 STORAGE                       at least 12 months (dry, cool and under cover )
 FLASH POINT                    23℃
 PACKAGING                     22kg
 
DIRECTIONS   Stir contents of each can thoroughly with a broad flat stirrer using a  stirring, lifting action or use a power mixer. Rate of cure will vary  depending on temperature and other factors such as ventilation, film  thickness, humidity, thinner. The temperature of stir will >15℃,  otherwise thinner should be added for needed viscosity after stir. 
 Overmuch thinner will lead sag and slow cure rate, thin film. Practical  spreading rates may be reduced 5—80% for wastage of different  application conditions. 
 
 
APPLICATION  STEEL: Round off all rough welds, sharp edges and remove weld spatter. Remove grease, oil and other contaminants. Steel surface must be prepared by abrasive blast cleaning to ISO Standard Class Sa2.5 or power tool cleaning Class St3.
Don’t apply at air temperature below 5℃ or above 40℃. Don’t apply at relative humidity above 85% or when air temperature is less than 3℃ above the dew point. 
Don’t apply if there is fog, rain, snow or strong wind. 
BRUSH/ROLLER: Suitable for small areas only. Apply even coats of the mixed material to the prepared surface. Thin if necessary with up to 0-15% with Chlorosulphonated Polythylene Thinner X-6. Additional coats may be required to attain specified thickness. 
CONVENTIONAL SPRAY: Thinning is not normally required, however 0-15% of Chlorosulphonated Polythylene Thinner X-6 can be added.
AIRLESS SPRAY: Thinning is not normally required, however 0-15% of Chlorosulphonated Polythylene Thinner X-6 can be added. Pump ratio is 23:1 or 32:1 and fluid tip is 0.38-0.43 mm.
Overcoating: Aged coating should be tested for lifting by a method such as ‘X’cut or crosshatch methods. If it lifts, remove it. The surface must be free of oil, grease and other contaminants.
Previous coat: Epoxy Coatings
CLEAN UP: with Chlorosulphonated Polythylene Thinner X-6

SAFETY:  Pay attention to the safety precautions before and after using this product. Users
 should comply with the provision of the respective country or local government. It’s
 dangerous or deadly to eating it. To avoid inhalation of thinner steams and spray mists.
Use protective wears correctly; the skin and eyes should avoid contacting it. Use with good ventilation. This product is flammable. All sources of ignition must be eliminated in, or near the working area. DO NOT SMOKE. Fight fire with foam, CO2 or dry chemical powder. On burning will emit toxic fumes.

Notes: The data in the manual is get from standard experiments and may be vary from different conditions in use. Please refer to the latest manual if the data is altered and we would not inform specially.